In Vitro Effect of Acidic Challenges on the Physical Properties of Dental Prosthesis Artificial Teeth

Abstract Objective: To evaluate the effect of immersion and acid challenge with cola drink on color change (ΔE), Vickers hardness (VHN) and surface roughness (Ra) of artificial acrylic resin teeth. Material and Methods: The artificial teeth were divided into 6 groups (n= 8): TC (Trilux/Control), BC (Biotone/Control), TAC (Trilux/Acid challenge), BAC (Biotone/Acid challenge), TI (Trilux/Immersion) and BI (Biotone/Immersion). The teeth were embedded in acrylic resin and the labial side was serially polished to provide appropriate flat surface. The samples of TC, BC, TI, BI groups were immersed in artificial saliva and cola drink (coke) for 7 days, respectively. The acid challenge was performed with immersion of samples in coke for 5 min, and subsequently immersion in artificial saliva for 2h. This cycle was repeated at 4 times/day, during 7 days. The tests of VHN, ΔE and Ra were analyzed before and after the challenge and immersion groups. Data was analyzed by ANOVA, Tukey and T test (α = 0.05). Results: There was no difference in Ra values between groups after treatments. However, there was a decrease in VHN for all groups. BI (19.2 ± 0.3) presented significantly lower hardness than BAC (19.5 ± 0.9) and BC (20.2 ± 0.5). Groups BI (2.18 ± 0.41) and TI (1.50 ± 0.43) had statistically higher ΔE compared to the other groups. Conclusion: The hardness of resin teeth decreased after acid challenges, but the roughness surface was not affected. The color was more affected by the times of exposure in cola beverage and remineralization in artificial saliva, which were associated to the material degradation (AU).

Os medicamentos infantis podem causar erosão na superfície de dentes decíduos? Revisão sistemática da literatura / Can child medications cause erosion on the surface of deciduous teeth? A systematic review of literature

Introdução: A erosão dentária é caracterizada por uma perda progressiva e irreversível dos tecidos dentários mineralizados que ocorre sem envolvimento bacteriano. Acredita-se que o uso frequente de medicamentos líquidos orais, em crianças, possa desenvolver erosão dentária visto que esses medicamentos apresentam, em sua maioria, pH ácido, que pode atuar como fator predisponente ao desenvolvimento da erosão dentária. Objetivo: O presente estudo avaliou os efeitos do uso de medicamentos líquidos orais na estrutura de dentes decíduos por meio de revisão sistemática da literatura. Material e Métodos: Foi realizada pesquisa de artigos científicos, em março de 2018, nas bases de dados PubMed e Web of Science utilizando descritores específicos para a pesquisa, de modo a avaliar, descritivamente, a seguinte pergunta "Os medicamentos infantis de uso contínuo podem causar erosão na superfície de dentes decíduos?" Foram encontrados 278 artigos na base de dados Pubmed e 41 na base Web of Science, dos quais 18 artigos eram coincidentes, assim 301 títulos e resumos foram lidos e analisados. Destes, 293 foram excluídos de modo que 8 artigos foram selecionados para análise crítica. Resultados: Os medicamentos líquidos de uso contínuo, geralmente utilizados para o tratamento de condições crônicas em crianças, promovem efeito erosivo sobre a estrutura dentária, principalmente quando relacionado ao pH e acidez titulável dos medicamentos, por avaliação de estudos conduzidos "in vitro". Conclusão: Torna-se necessária a realização de estudos clínicos para avaliação mais adequada do efeito erosivo de medicamentos infantis na superfície de dentes decíduos.

Introduction: Dental erosion is characterized by a progressive and irreversible loss of mineralized dental tissues that occurs without bacterial involvement. It is believed that the frequent use of oral liquid medicines in children can develop dental erosion since the majority of these medications has acidic pH, which can act as a predisposing factor for dental erosion development. Objective: The present study evaluated the effects of the use of liquid oral medications on the structure of deciduous teeth by a systematic review of literature. Material and Methods: We conducted a survey of scientific articles in PubMed and Web of Science databases on March 2018, using specific descriptors for the research, in order to evaluate descriptively the following question: "Children's medicines for continuous use may cause erosion on the surface of deciduous teeth?". We found 278 articles in the PubMed database and 41 in the Web of Science database, of which 18 articles were matched, so 301 titles and abstracts were read and analyzed. Of these, 293 were excluded. Thus, 8 articles were selected for the critical analysis. Results: Liquid medications of continuous use, generally used for the treatment of chronic conditions in children, promoted erosive effect on dental structure, especially when related to pH and titratable acidity of the drugs in in vitro studies. Conclusion:It is necessary to carry out clinical studies for a more adequate evaluation of the erosive effect of children's medicines on the surface of deciduous teeth.

Qual material possui maior longevidade em molares decíduos: resina composta ou cimento de ionômero de vidro? - revisão sistemática da literatura / Which material has the highest longevity in primary molars: composite resin or glass ionomer cement? - a systematic review of the literature

Introdução: Diversos materiais restauradores são indicados para a restauração de dentes decíduos posteriores, como amálgama, resina composta, cimento de ionômero de vidro convencional, cimento de ionômero de vidro modificado por resina e resinas compostas modificadas com poliácidos (compômeros). Entretanto, uma dúvida ainda persiste quanto ao desempenho clínico do cimento de ionômero de vidro, em decorrência de suas propriedades, para ser utilizado como material restaurador definitivo em molares decíduos. Objetivo: Realizar uma revisão sistemática da literatura acerca da taxa de sobrevivência de restaurações realizadas em molares decíduos utilizando resina composta e cimento de ionômero de vidro, buscando com base em evidências científicas, responder a PICO question: "Qual material possui maior longevidade em molares decíduos: resina composta ou cimento de ionômero de vidro?". Material e métodos: Para este fim foram realizadas buscas em duas bases de dados, PubMed e Web of Science, utilizando uma estratégia de busca previamente determinada, para selecionar artigos de acordo com critérios de inclusão e exclusão criados para esse trabalho por dois examinadores calibrados. Resultados: A seleção dos artigos foi realizada de acordo com o fluxograma do PRISMA e foi criada uma tabela para avaliação qualitativa dos artigos selecionados. Foram encontrados 398 artigos na base de dados PubMed e 375 na Web of Science, sendo 153 coincidentes em ambas. Quarenta e seis artigos foram selecionados para leitura completa, dentre eles 42 foram excluídos, e quatro artigos foram incluídos para esta revisão. Conclusão: Os artigos desta revisão demonstraram que a resina composta possuiu maior longevidade em molares decíduos comparada aos cimentos de ionômero de vidro. Porém futuros estudos clínicos necessitam ser conduzidos para comprovar qual o material mais indicado para restaurá-los, já que os cimentos de ionômero modificados por resina mostraram taxas de sobrevivência clínica satisfatórias.

Introduction: Several restorative materials are indicated for restoration of posterior deciduous teeth, such as amalgam, composite resin, conventional glass ionomer cement, resin modified glass ionomer cement and composite resins modified with polyacids (compomers). However, a doubt still persists related to the clinical performance of the glass ionomer cements to be used to restore deciduous molars, due to its properties. Objective: To perform a systematic review of the literature about the survival rate of composite resin and glass ionomer cement restorations performed in deciduous molars aiming scientific evidence to answer the PICO question: "Which material has greater longevity in deciduous molars: resin composite or glass ionomer cement?" Material and methods: The research was performed on two databases, PubMed and Web of Science, using a predetermined search strategy to select articles according to the inclusion and exclusion criteria, evaluated by two calibrated examiners. Results: The selection of the articles was carried out according to the PRISMA flowchart and a table was created for the qualitative evaluation of the included articles. It was found 398 articles in the PubMed database and 375 in the Web of Science, 153 of which were coincident in both. Forty-six articles were selected for complete reading, 42 of which were excluded, and four articles were included in this review. Conclusion: The articles investigated in this review demonstrated that composite resin has a higher longevity in deciduous molars compared to glass ionomer cements. However, future clinical studies are needed to attest which material is better to restore them, since the resin modified glass ionomer cements showed satisfactory clinical survival rates.